Klubersynth BHP 72-102 High temperature grease 500g cartridge, Kluber Lubrication 0941020594
Available from factory - Estimated to ship in: 21 days.
Klubersynth BHP 72-102, High-temperature lubricant with extraordinary anticorrosion properties for lifetime lubrication, 500g, Kluber Lubrication PN: 0941020594
The Benefits
- Long availability of components over a wide service temperature range: when exposed to corrosive atmosphere, when exposed to high vibrations and loads.
- High economic efficiency due to innovative hybrid grease formulation.
The Solution
Klübersynth BHP 72-102 is an innovative, synthetic long-term lubricating grease based on ester oils and perfluorinated polyether oil (PFPE). Its outstanding characteristics are good oil retention at high permanent temperatures and good corrosion protection as well as water resistance - yet another contribution to a longer bearing life and a higher thermal stability compared to conventional lubricants. In tests performed on component test rigs subject to high permanent temperatures up to 200 °C Klübersynth BHP 72-102 offers an extremely long service life.
Application
Klübersynth BHP 72-102 has been designed for the lifetime lubrication of rolling bearings subject to high loads and alternating temperatures ranging from -40 °C to 200 °C. The product is suitable for the lubrication highly loaded rolling bearings in components close to automobile engines, e.g. bearings viscocouplings, belt tensioners, water pumps, fans, servomotors and similar applications. Klübersynth BHP 72-102 forms a stable grease collar that serves as a lubricant reservoir resistant to vibration and at the same time helps to protect the bearings against contaminants.
Application notes
Klübersynth BHP 72-102 can be applied by standard metering systems (brush, spatula, grease gun). Ideally, the bearing should be metallically blank. If any anticorrosive fluid has been applied prior to greasing, we recommend checking compatibility with the lubricant.
More Information
| Characteristics | Item Info |
| Composition, thickener | polyurea |
| Composition, type of oil | ester oil , PFPE |
| Colour space | white |
| Service temperature, lower limit | -40 °C |
| Service temperature, upper limit | 200 °C |
| Density, Klüber method: PN 024, 20°C | approx. 1.3 g/cm³ |
| Worked penetration, DIN ISO 2137, 25 °C, lower limit value | 240 0.1 mm |
| Worked penetration, DIN ISO 2137, 25 °C, upper limit value | 270 0.1 mm |
| Shear viscosity, Klüber method: PN 008@DIN 53019-1, equipment: rotational viscometer, 25°C, 300 s⁻¹, lower limit | 4000 mPas |
| Shear viscosity, Klüber method: PN 008@DIN 53019-1, equipment: rotational viscometer, 25°C, 300 s⁻¹, upper limit | 8000 mPas |
| Kinematic viscosity of the base oil, DIN EN ISO 3104 / DIN 51562-1 /ASTM D445 / ASTM D7042, 100°C | approx. 20 mm²/s |
| Kinematic viscosity of the base oil, DIN 51562 pt. 01/ASTM D-445/ASTM D 7042, 40 °C | approx. 130 mm²/s |
| Copper corrosion, DIN 51811, 24 h, 100°C | 1 - 100 - 24 corrosion degree |
| SKF-EMCOR, DIN 51802, based on standard, Klüber method: 3 % NaCl solution, 168 h | ≤ 3 corrosion degree |
| Flow pressure, DIN 51805-2, -35°C | ≤ 1400 mbar |
| Dropping point, DIN ISO 2176 / IP 396 | ≥ 240 °C |
| Speed factor (n x dm) | approx. 1000000 mm/min |
| Minimum shelf life from the date of manufacture - in a dry, frost-free place and in the unopened original container, approx. | 36 months |